I repeated the PLA in acetone experiment with red PLA and pure acetone. Same result, trifurcation after a few minutes:

Here is what happens to an object:

These were identical PLA clothes-pegs, one was dipped in acetone for a few minutes.  It fell apart when I tried to pick it out with tongs.

A bit of Googling reveals acetone causes PLA (which is normally amorphous) to become crystalline. That explains why it loses its transparency I think. It also becomes rubbery and crumbly.

Not a very useful result, but it does show that acetone would not be any good for cleaning out a hot end filled with PLA. Also I think people have suggested you could use ABS as support for PLA and dissolve it out with acetone but that plainly will not work either. The opposite works, dissolving the PLA with an alkali.

Peeled PLA

I have read conflicting forum posts as to whether acetone dissolves PLA or not, so I dropped a piece into a jar of acetone for an hour or so. The effect was truly bizarre:

It split into three strands a bit like peeling a banana. It was clear PLA but the acetone was polluted with ABS, which is why it turned white I think. Whereas it is normally transparent and brittle, it has become translucent soft and flexible. When I opened the jar it was under pressure so I think it evolved some gas.

So acetone doesn't dissolve PLA, but it appears to trifurcate it!

Not a very scientific experiment as I should have done it with pure acetone, but interesting never the less.

Glossy

I downloaded this clever object from Thingiverse. It was created by wizard23 using a parametric CSG evaluator plugin for ArtOfIllusion that he and the other the guys at MetaLab are developing.



The two halves screw together and fit perfectly.



I gave it a glossy finish by painting it with acetone. It looks like it is still wet but it actually dries almost instantly.